Hyeong-Yeon Lee
The Journal of Mechanical Science and Technology, vol. 22, no. 5, pp.856-863, 2008

Abstract : The ASME draft Code Case for Alloy 617 was developed in the late 1980s for the design of very-high-temperature gas cooled reactors. The draft Code Case was patterned after the ASME Code Section III Subsection NH and was intended to cover Ni-Cr-Co-Mo Alloy 617 to 982°C (1800°F). But the draft Code Case is still in an incomplete status, lacking necessary material properties and design data. In this study, a preliminary evaluation on the creep-fatigue damage for a high temperature hot duct pipe structure has been carried out according to the draft Code Case. The evaluation procedures and results according to the draft Code Case for Alloy 617 material were compared with those of the ASME Subsection NH and RCC-MR for Alloy 800H material. It was shown that many data including material properties, fatigue and creep data should be supplemented for the draft Code Case. However, when the evaluation results on the creep-fatigue damage according to the draft Code Case, ASME-NH and RCC-MR were compared based on the preliminary evaluation, it was shown that the Alloy 617 results from the draft Code Case tended to be more resistant to the creep damage while less resistant to the fatigue damage than those from the ASME-NH and RCC-MR.

Keyword : Creep-fatigue; High temperature design code; Alloy 617; Alloy 800H; Very high temperature reactor; Hot gas duct